L-9211W Water-based PU Plastic Primer hydroxyl-containing acrylic resin for two-component water-based plastic primer
L-9211W is a hydroxyl-containing acrylic resin dispersion modified by a special process. It has the characteristics of good adhesion, quick drying, high transparency, good gloss, and good pigment wettability. L-9211W can be mixed with water-based isocyanate curing agent to prepare two-component industrial paint and automotive repair paint, or mixed with amino resin to prepare high-temperature baking paint, with excellent water resistance, solvent resistance and weather resistance.
Appearance | Milky white lotion |
Viscosity(mPa.s) | 400-3,000 |
Solid content % | 45±1 |
Hydroxyl content | 1.1 |
pH value | 7.5±0.5 |
Average particle size (nm) | 100-120 |
It has high bearing capacity for pigments and fillers, good adhesion to ABS, ABS/PC, PC, wood, and metal, and has excellent flexibility, water resistance, scrub resistance, and alkali resistance. Especially the adhesion to plastic is good.
Product | Description | Properties & Applications |
L-9203W | Water-based Metal Paint Resin | L-9203W is used for water-based PU topcoat, with high cost performance and good weather resistance |
L-9211W | Water-based PU Plastic Primer Resin | L-9211W water-based PU plastic primer is cost-effective, has good adhesion and has good overall performance |
L-9400W | PU Quick-drying Wear-resistant Resin | L-9400W is quick drying and has good wear resistance |
L-9500W | Water-based PU High Wear-resistant Resin | L-9500W has high hydroxyl group, high fullness, good wear resistance and good chemical resistance |