| Customization: | Available |
|---|---|
| CAS No.: | / |
| Formula: | / |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Appearance | Slightly transparent liquid | |
| Viscosity (Iwata - 2 cups) | 8.5-9.5 S | |
| UV component (%) | 35±2 % | |
| Density (g/cm³, 25ºC) | 0.90±0.05 | |
| Coating performance | ||
| Hardness (1Kg force load) | 3H-5H | |
| Coating thickness (μm) | 5-15 | |
| Boiling performance (surface spray paint, no primer 100ºC/60min) | Adhesion 5B, no change in coating | |
| Bending (cylindrical shaft diameter) | 40mm | |
| Curing energy (mercury lamp, mj/cm²) | 600-1,000 | |
| QUV resistance | More than 500h | |
| Anti-friction performance (1Kg load-bearing, wear-resistant machine, 1*1 grinding head, 0000# steel wool) | 2500 times, no wear marks | |
| Anti-graffiti (Zebra oil-based pen) | Oleophobic lines, easy to wipe off | |
| Water contact angle | 105-110° | |
| Note: The above performance parameters can be customized according to customer requirements | ||
Texture decoration and shell molding of mobile phones, laptops, home appliances and other products.
1. The commonly used coating methods for UV wear-resistant hardening fluid are spraying, shower coating, and roller coating. Please avoid exposure to sunlight;
2. The product does not require any pre-treatment (including dilution). It is recommended to shake before coating to make the dispersion more even;
3. When performing shower coating, the nozzles of the shower coating equipment should be sprayed from the same horizontal line from left to right. Please refer to the equipment manufacturer's instructions for the specific process;
4. After the shower coating is completed, keep the plate running vertically for about 2 minutes to allow the surface to evaporate and level, then enter the 60-70°C drying tunnel and keep it vertically heated for 5 minutes;
5. After heating, enter the UV curing lamp area for routine curing. The specific curing time is recommended to be adjusted according to the energy of the lamp. If conditions permit, the time can be extended appropriately, which will help improve the hardness of the film layer; (The energy of the UV curing lamp during the test experiment was 2000W. Lamp tube length 30cm)
6. After curing, cool the plate to room temperature and then measure its performance directly;
7. Please clean the equipment thoroughly with organic solvent after curtain coating.
1. This product has been diluted to a solid content and viscosity suitable for shower coating, and does not need to be diluted before use. If customers need high solid content and dilutable products, our company can provide corresponding high solid content products and corresponding diluents according to the customer's specific requirements;
2. This product contains flammable components, please pay attention to fire prevention during transportation, storage and use.
1) Are you a factory or trading company ?
A: We are a professional factory with over 5 years producing experience.
){kind=link}